Nitrogen-doped cobalt sulfide as an efficient electrocatalyst for hydrogen evolution reaction in alkaline and acidic media

The enhancement in intrinsic catalytic activity and material conductivity of an electrocatalyst can leads to promoting HER activity. Herein, a successful nitrogenation of CoS₂ (N–CoS₂) catalyst has been investigated through the facile hydrothermal process followed by N₂ annealing treatment. An optimized N–CoS₂ catalyst reveals an outstanding hydrogen evolution reaction (HER) performance in alkaline as well as acidic electrolyte media, exhibiting an infinitesimal overpotential of ?0.137 and ?0.097 V at a current density of ?10 mA/cm² (?0.309 and ?0.275 V at ?300 mA/cm²), corresponding respectively, with a modest Tafel slope of 117 and 101 mV/dec. Moreover, a static voltage response was observed at low and high current rates (?10 to ?100 mA/cm²) along with an excellent endurance up to 50 h even at ?100 mA/cm². The excellent catalytic HER performance is ascribed to improved electronic conductivity and enhanced electrochemically active sites, which is aroused from the synergy and mutual interaction between heteroatoms that might have varied the surface chemistry of an active catalyst.     

Grain orientation evolution and multi-scale interfaces enhanced thermoelectric properties of textured Sr0.9La0.1TiO3 based ceramics

Sr_0.9La_0.1TiO₃ based textured ceramics (SLTT-S3T) with a texture fraction of 0.81 are successfully fabricated by the reactive template grain growth method, in which Sr_0.9La_0.1TiO₃/20 wt%Ti was used as matrix and 10 wt% plate-like Sr₃Ti₂O₇ template seeds were used as templates. The phase transition, microstructure evolution, and the anisotropic thermoelectric properties of SLTT-S3T ceramics were investigated. The results show that the ceramics are mainly composed of Sr_0.9La_0.1TiO₃ and rutile TiO₂ phases. Grains grow with a preferred orientation along (h00). A maximum ZT of 0.26 at 1073 K was achieved in the direction perpendicular to the tape casting direction. The low lattice thermal conductivity of 1.9 W/(m K) at 1073 K was obtained decreased by 34%, 40%, and 38% compared with non-textured, SrTiO₃ and Sr_0.9La_0.1TiO₃ ceramics prepared by the same process, can be attributed to the enhanced phonon scattering by the complex multi-scale boundaries and interfaces. This work provides a strategy of microstructural design for thermoelectric oxides to decrease intrinsic lattice thermal conductivity and further regulate thermoelectric properties via texture engineering.     

Spray pressure variation effect on the properties of CdS thin films for photodetector applications

Herein, we report the photosensing property of CdS thin films. CdS thin films were coated onto glass substrates via a spray pyrolysis method using different spray pressures. Prepared films were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and optical and photoluminescence spectroscopy. XRD analysis demonstrated the growth of crystalline CdS films with crystallite sizes varying from 26 to 29 nm depending on the pressure. The SEM and EDAX analyses revealed nearly-stoichiometric CdS films with smooth surfaces and slight variation in grain morphology due to pressure changes. Optical measurements showed a direct bandgap varying from 2.37 eV to 2.42 eV due to pressure changes. A photodetector was also fabricated using the grown CdS films; the fabricated photodetector exhibited good performance depending on the spray pressure. A spray pressure of 1.5 GPa resulted in high photoresponsivity and external quantum efficiency.     

Sputtered Ir–Ru based catalysts for oxygen evolution reaction: Study of iridium effect on stability

Magnetron sputtered low-loading iridium-ruthenium thin films are investigated as catalysts for the Oxygen Evolution Reaction at the anode of the Proton Exchange Membrane Water Electrolyzer. Electrochemical performance of 50 nm thin catalysts (Ir pure, Ir–Ru 1:1, Ir–Ru 1:3, Ru pure) is tested in a Rotating Disk Electrode. Corresponding Tafel slopes are measured before and after the CV-based procedure to compare the activity and stability of prepared compounds. Calculated activities prior to the procedure confirm higher activity of ruthenium-containing catalysts (Ru pure > Ir–Ru 1:3 > Ir–Ru 1:1 > Ir pure). However, after the procedure a higher activity and less degradation of Ir–Ru 1:3 is observed, compared to Ir–Ru 1:1, i.e. the sample with a higher amount of unstable ruthenium performs better. This contradicts the expected behavior of the catalyst. The comprehensive chemical and structural analysis unravels that the stability of Ir–Ru 1:3 sample is connected to RuO₂ chemical state and hcp structure. Obtained results are confirmed by measuring current densities in a single cell.     

The superlattice structure and self-adaptive performance of C–Ti/MoS2 composite coatings

To improve the self-adaptability of MoS₂ coating in different environments, the coatings were doped with functional C and Ti by unbalanced magnetron sputtering system. The clear superlattice structure with minimal modulation period was investigated by High Resolution Transmission Electron Microscope (HRTEM). The co-doped coatings have better mechanical properties due to the special structure and the formation of C–Mo, Ti–S and Ti–O bonds, and better lubrication performance in both high humidity and vacuum than those of the single-doped ones. The doped Ti not only facilitates the formation of the MoS₂ (002) basal plane, but also improves the oxidation resistance of the composite film. The degree of friction-induced graphitization on the wear tracks and the quality of transfer films on the wear scars are key factors affecting the lubrication performance of the composite film. In the high-humidity environment, the reasonable doping elements can promote the formation the high-quality transfer film by interacting with H₂O water molecules, which will benefit the lubrication of the coating better. Our findings deepen the understanding of MoS₂ composite coating and provide a new solution for improving the self-adaptability of the coating.     

模内装饰薄膜滞热对成型工艺的影响分析

以模内装饰技术(IMD)测试平板为研究对象，利用仿真和实验方法分析薄膜滞热的影响因素及薄膜滞热对成型工艺的影响规律。结果表明，薄膜滞热使动模侧模具温度场变化滞后于定模侧温度场，且在实验条件下达到8.6 ℃的最大温度差；薄膜滞热随着模具温度的增加而降低，随熔体温度和薄膜厚度增加而升高；薄膜影响熔体的充模与冷却，造成产品冷却不均的现象；薄膜滞热导致产品翘曲变形增加。     

Effects of the film thickness and poling electric field on photovoltaic performances of (Pb,La)(Zr,Ti)O3 ferroelectric thin film-based devices

The ferroelectric photovoltaic (FPV) effect obtained in inorganic perovskite ferroelectric materials has received much attention because of its large potential in preparing FPV devices with superior stability, high open-circuit voltage (V_oc) and large short-circuit current density (J_sc). In order to obtain suitable thickness for the ferroelectric thin film as light absorption layer, in which, the sunlight can be fully absorbed and the photo-generated electrons and holes are recombined as few as possible, we prepare Pb_0.93La_0.07(Zr_0.6Ti_0.4)_0.9825O₃ (PLZT) ferroelectric thin films with different layer numbers by the sol-gel method and based on these thin films, obtain FPV devices with FTO/PLZT/Au structure. By measuring photovoltaic properties, it is found that the device with 4 layer-PLZT thin film (~300 nm thickness) exhibits the largest V_oc and J_sc and the photovoltaic effect obviously depends on the value and direction of the poling electric field. When the device is applied a negative poling electric field, both the V_oc and J_sc are significantly higher than those of the device applied the positive poling electric field, due to the depolarization field resulting from the remnant polarization in the same direction with the built-in electric field induced by the Schottky barrier, and the higher the negative poling electric field, the larger the V_oc and J_sc. At a -333 kV/cm poling electric field, the FPV device exhibits the most superior photovoltaic properties with a V_oc of as high as 0.73 V and J_sc of as large as 2.11 μA/cm². This work opens a new way for developing ferroelectric photovoltaic devices with good properties.     

Irradiation-induced large bubble formation and grain growth in super nano-grained ceramic

In this work, 0.5TRPO•0.5Gd₂Zr₂O₇ ceramic with an average grain size of only ∼15 nm was prepared by a high pressure (5 GPa/520 °C) sintering method. Phase evolutions and microstructure changes of the as-fabricated super nano and micron-grained ceramics under a high-dose displacement damage induced by 300 keV Kr²⁺ ions were investigated. The results show that the super nano-grained ceramic has low degree of amorphization, obvious grain growth (2–3 times in grain size) and big Kr bubbles (10–68 nm) formation after irradiation. The micron-grained ceramic was severely amorphized after irradiation and many microcracks were formed parallel to its surface. The formation mechanism of Kr bubbles in the super nano-grained ceramic is on account of grain boundary diffusion and migration induced by the accumulation of the injecting Kr ions and irradiation defects. Nevertheless, microcracks formed in the micron-grained sample are caused by the accumulation of Kr atoms.     

Fabrication of Cu/graphite film/Cu sandwich composites with ultrahigh thermal conductivity for thermal management applications

Effective thermal management of electronic integrated devices with high powder density has become a serious issue, which requires materials with high thermal conductivity (TC). In order to solve the problem of weak bonding between graphite and Cu, a novel Cu/graphite film/Cu sandwich composite (Cu/GF/Cu composite) with ultrahigh TC was fabricated by electro-deposition. The micro-riveting structure was introduced to enhance the bonding strength between graphite film and deposited Cu layers by preparing a rectangular array of micro-holes on the graphite film before electro-deposition. TC and mechanical properties of the composites with different graphite volume fractions and current densities were investigated. The results showed that the TC enhancement generated by the micro-riveting structure for Cu/GF/Cu composites at low graphite content was more effective than that at high graphite content, and the strong texture orientation of deposited Cu resulted in high TC. Under the optimizing preparing condition, the highest in-plane TC reached 824.3 W·m⁻¹·K⁻¹, while the ultimate tensile strength of this composite was about four times higher than that of the graphite film.     

Economic growth,CO2 emissions,and energy consumption in the five ASEAN countries

This paper investigates the relationship between economic growth, carbon dioxide (CO₂) emissions, and energy consumption with an aim to test the validity of the Environmental Kuznets Curve (EKC) hypothesis in five ASEAN (Association of South East Asian Nations) countries (Indonesia, Malaysia, Philippines, Singapore, and Thailand) by applying the panel smooth transition regression (PSTR) model as a new econometric technique. The PSTR model is more flexible and appropriate for describing cross-country heterogeneity and time instability. Our empirical results strongly rejected the null hypothesis of linearity, and the test for no remaining nonlinearity indicated a model with one transition function and two threshold parameters. The first regime (levels of GDP per capita below 4686 USD) showed that environmental degradation increases with economic growth while the trend was reversed in the second regime (GDP per capita above 4686 USD). The results also showed that energy consumption with either the first or the second regime lead to increase CO₂. The overall results support the validity of the EKC hypothesis in the ASEAN countries.